SUMMARY
The study on the posibility of the use of the optimal glass compositions for vitrification of an imitator of vat residues of liquid radioactive waste from nuclear power plants with VVER-1000 reactors was carried out. The main process parameters such as vitrification temperature, strength, corrosion resistance, absence of crystalline phases, minimization of glass-forming additives and inclusion the maximum amount of waste were analyzed. It has been established that the melting temperature of lead-borosilicate glass matrices was 1150 °C, which satisfies the requirements for vitrification of low- and medium-level waste. The ultimate compressive strength of the obtained samples of glass matrices was 136.0 MPa. In addition, it has been shown that lead-borosilicate glass matrices are the most resistant to leaching. The cesium leaching rate was 1.5·10-5 g/cm2·day.