Fabrication and Evaluation of the Photocatalytic, Antibacterial Activity of Ag–TiO2_2 Thin Film

SUMMARY

Ag–TiO2 thin film was fabricated by DC magnetron sputtering and photoreduction methods. Characteristics of the film such as surface area, crystal structure, and chemical composition were investigated by using scanning electron microscope (SEM), X–ray diffractometry (XRD) and UV–vis spectra. The photocatalytic activity of Ag–TiO2 thin film was determined by the degradation of methylene blue (MB) solution under various irradiation conditions. The antibacterial property of Ag–TiO2 thin film was conducted in E. coli bacteria. Results showed that the photocatalytic and antibacterial property of Ag–TiO2 thin film are better than those of pure TiO2 thin film in the visible region. Ag–TiO2 thin film shows a great potential application in the antibacterial and environment field.

PAGES
pp. 233
COLLECTIONS
Physical

 Articles related

Agus Andi Wibowo    

Zinc Oxide doped Gallium Oxide (Ga2O3:Zn) thin films have been successfully deposited at corning glass and silicon (1 1 1) substrat with a plasma power 20.16 W with substrat temperature 600°C dan 635°C using dc magnetron sputtering method. The crystal st... see more


Le Phuc Quy,Vu Thi Hanh Thu    

TiO2_2 thin films are used for oxidation of organic radicals, reducing CO2_2, skin cancer treatment, decomposing halogen compounds in the air, breaking down surface contaminants, water treatment, biodegradable oil on the surface of the water, disinfect, ... see more


kiki wahyuningsih, Putut Marwoto, - Sulhadi    

zinc oxide thin films have been successfully deposited at room temperature with a plasma power 20 W, 30 W, and 40 W using dc magnetron sputtering method. The crystal structure of films were characterized using XRD (X-ray diffraction). Optical transmittan... see more


S. Sulhadi,F. Fatiatun,P. Marwoto,S. Sugianto,E. Wibowo    

Telah dilakukan deposisi film tipis ZnO:Ga di atas substrat kaca korning pada tekanan deposisi 500 mtorr dengan metode DC-magnetron sputtering. Film ditumbuhkan masing-masing pada suhu 325oC, 375oC, dan 425oC. Struktur, sifat optik dan sifat listrik film... see more


P. Marwoto,N.M. Darmaputra,Sugianto -,Z. Othaman,E. Wibowo,S.Y. Astuti    

Film tipis CdTe dengan doping tembaga (Cu) berkonsenterasi 2% telah berhasil ditumbuhkan di atas substrat Indium Tin Oxide (ITO) dengan metode dc magnetron sputtering. Penelitian ini dilakukan untuk mengetahui pengaruh doping Cu(2%) terhadap struktur mor... see more